Designation
- Grade
- CN7M
- UNS
- N08007
- Standard
- ASTM A351/A351M, A743/A743M, A744/A744M
- Density
- ≈ 8.00 g/cm³
- Usual delivery condition
- Solution annealed and quenched
Chemical composition
| Element | Mass fraction, % |
|---|---|
| C | ≤ 0.07 |
| Mn | ≤ 1.50 |
| Si | ≤ 1.50 |
| Cr | 19.0–22.0 |
| Ni | 27.5–30.5 |
| Mo | 2.0–3.0 |
| Cu | 3.0–4.0 |
| Fe | bal. |
Main elements only. Phosphorus, sulphur and residual-element limits are specified in the standard and are not reproduced here.
Mechanical properties
| Condition | Tensile strength Rm, min. (MPa) | Yield strength Rp0.2, min. (MPa) | Elongation, min. (%) |
|---|---|---|---|
| Solution annealed and quenched | 425 | 170 | 35 |
Minimum values (or ranges) for separately cast test bars as specified in ASTM A351/A351M, A743/A743M, A744/A744M.
Characteristics
- Corrosion and oxidation behaviour
- Selected for acids and aggressive chemical process media
- Weldability
- Possible with qualified procedure; preheat and/or post-weld heat treatment as specified
- Machinability
- Moderate; work hardening or built-up edge to be considered
- Typical applications
- Valves Pumps Chemical processing
International cross-reference
| System | Designation | Relationship |
|---|---|---|
| UNS (wrought) | N08020 (Alloy 20) | Comparable properties |
Casting and processing considerations
Castings are normally solution annealed and rapidly cooled to dissolve carbides and restore corrosion resistance. Low-carbon grades are preferred where castings will be welded without subsequent heat treatment. High shrinkage requires adequate feeding of heavy sections; surface finish and pickling or passivation requirements should be agreed in advance.
Reference data compiled from the cited standards for orientation. Always work from the current edition of the governing specification; values are not a guaranteed LOSTWAX delivery specification.